Vicell B-series Balsa TDS
Core Material Expert -- always beyond excellence
Products
Vicell B-series Balsa TDS
Core Material Expert -- always beyond excellence
模具：手糊、rtm用玻璃钢模具，尺寸稳定性好
Mould: hand lay-up, rtm glass fiber reinforced plastics mould with favorable size and stability
船舶：船壳、尾封板、龙骨、甲板、上层结构、舱壁等
Shipping: hull,stern transom plate,keel, deck, upper structure, bulkhea
军舰：上层结构、舱壁、甲板、整流装置
Warship: upper structure, bulkhead,deck,rectifying device
铁路：导流罩、地板、墙壁、门、顶板、内隔板
Railway: fairing, floor, wall, door, ceiling,inner diaphragm
汽车：地板、顶板、单壳体车身结构
Automobile: floor, ceiling,monocoque body
航空：地板、内隔板、货舱及集装箱
Aviation: floor, inner diaphragm, cargo chamber, containers
工业：风力叶片、导流罩、防腐罐、管道
Industries: wind power blades, fairing cover, antiseptic pot and pipeline
建筑：混凝土结构、轻质结构以及建筑模板
Architecture: concrete construction, light structure and building templates
军事：战术掩体、货舱及集装箱
Military: blindage, cargo and container
体育：滑雪板、滑水板等
Sports: ski and water ski boards
其它：撞击与反冲测试设备
Others: impact and test equipment
项目 Item | 测试标准 Test standard | 单位 Unit | B100 | B130 | B150 | |||
标称密度 Apparent nominal density | ISO 845 | Kg/m3 | 100 | 130 | 150 | |||
密度范围 Range density | ISO 845 | MPa | 85-110 | 110~135 | 135~176 | |||
含水率 Moisture content | GB/T1931 | % | ≤12 | ≤12 | ≤12 | |||
压缩强度Z Compression strength Z | ISO 844 | MPa | 5 | 7.8 | 10.0 | |||
压缩模量Z Compression modulus Z | ISO 844 | MPa | 1600 | 2200 | 3000 | |||
拉伸强度Z Tensile strength Z | ASTM C297 | MPa | 8 | 9 | 10 | |||
拉伸模量Z Tensile modulus Z | ASTM C297 | MPa | 1800 | 2350 | 3000 | |||
剪切强度XZ、YZ Shear strength XZ、YZ | ISO 1922 | MPa | 1.8 | 2.1 | 2.60 | |||
剪切模量XZ、YZ Shear modulus XZ、YZ | ISO 1922 | MPa | 140 | 160 | 180 | |||
|
|
|
|
|
| |||
标准板材Standard sheet | Length（mm） | 1220 | tolerance | ±2mm | ||||
Width（mm） | 610 | tolerance | ±2mm | |||||
包装Package | 包装采用标准的防护措施进行包装，包装箱密封严密，适合整体吊装。良好的防潮、防冲击、非法装卸保护措施，确保货物安全运送到用户现场。 The packaging is packaged with standard protective measures, and the packaging box is tightly sealed and suitable for overall hoisting.Good protection measures against moisture, shock and illegal loading and unloading to ensure the safe delivery of goods to the user site. | |||||||
储存Storage
| 将材料包装在纸板或塑料板中，防止水分、灰尘、阳光直射和碰撞。贮存温度应低于50℃，相对湿度应为30%-80%，并应密封良好，控制巴尔萨的含水量以满足要求。同时，沥青木板不得有挤压、变形、开裂等缺陷，存放车间需要设置相应的防火设施。Pack the material in cardboard or plastic sheeting to keep it out of moisture, dust, direct sunlight and bumps.The storage temperature should be lower than 50℃, the relative humidity should be 30%-80%, and it should be well sealed to control the moisture content of Balsa to meet the requirements.At the same time, Balsa wood panels shall not be squeezed, deformed, cracked and other defects; corresponding fire prevention facilities are required in the storage workshop. | |||||||
Note: 1. The data provided are approximate test values for nominal density. Due to variations in density, some test values may be lower than those shown in the table above.
2. Tensile property tests are performed without glass fiber skin.